Manufacture and supply Zirconia Powder, Zirconium Chemicals, Advance Ceramics, Industrial Minerals by Raj Purohit Group of Enterprises in India. Mineral Processing Company as Advance Ceramic Materials, Industrial Minerals.
Profile Products Particle Technology Centre Inquiry Site Map Contact
Zirox -CP
 Co-precipitated zirconia powders 
3 Mol% Yttria Stabilized Tetragonal Zirconia
Powders ( TZP)
Zirox -CP-TZY-3n
Sinterable at 1350'C without Binder
Zirox-CP TZY-3nSB
Sinterable at 1350'C,Spray Dried with Binder
Sinterable at 1450 1530'C,without Binder
Spray Dried with Binder, Sinterable at 1450-1530'C
Monoclinic Zirconia Powders
monoclinic zirconia
nano monoclinic zirconia
8 Mol% Yttrium Fully
Stabilized Zirconia
Zirox-CP-FZY 8n
Thermal Zirconia Powders
Monoclinic zirconia
nano Monoclinic Zirconia
submicronised zirconia
3um zirconia
325 mesh zirconia
granular zirconia
Monoclinic zirconia
7-8% yttria stabilized Zirconia
TZY-TBC-SDP -8% yttria     Stabilized- Spray Dried Zirconia
Zirconia Toughened Alumina(s)
Nano ZTA
Zirox CP-ZTA
(Sinterable at 1560'C)
(Ready to press)
Rare Earths
Yttrium Oxide
Cerium Oxide
Technology & applications of Zirconia powder
Zirconia beads & ceramic components
Zirconia Beads- YZB
Dental Blanks
Nano Dispersions & Powders
- TI 205
Nano Titanium Oxide
Nano Zinc Oxide dispersion
Nano Zirconium Oxide
-ZR 105
nano monoclinic zirconia dispersion

nano monoclinic zirconia
nano Tetragonal zirconia dispersion
Industrial Minerals
Zircon Sand
Zircon Flour
Zirconium Silicate-5
GCC-Ground Calcium
Carbonate Powders
5um Coated
15um Uncoated
Calcia- Nano -
Ground Calcium Carbonate
    Wollsill-HAR- High Aspect Ratio
Wollsill-FBRS -
Medium Aspect Ratio

Wollsill-LL -
Low Aspect Ratio
Kaolin 86n
Kaolin 82
Silica ( Quartz) powders
(3um average particle powder)
(6um average particle powder)
Potash Feldspar
Sodium Feldspar
Particle Technology Centre
Ziroxmill-UFM technology
Nano Zirconia Solutions
Nano Dispersion   Nano Powders  Nano Solutions  Nano Materials
Properties of nano zirconia dispersions &
nano zirconia powders
unit Values of different nano zirconia grades
  NZ-m NZ-m aqasol NZ-3YSZ NZ-3YSZ
Specific surface area(BET) M2/g 60   60  
Average primary particle size nm 12   12  
Taped density(apprx. value)
Acc. To DIN EN ISO 787/11 august 1983
g/l Appr.100   Appr 1.00  
Moisture,2 hours at 105’C Wt.% 02.00   02.00  
Loss on ignition
2 hours at 1000’C based on the material dried  for 2 hours at 105’C
Wt% 03.00   3.00  
Ph in 4% dispersion / DIN ES ISO 787/9   04-06 08-10 04-06 09-11
ZrO2 contents Wt% 97.00 50.0 92.00 50
Y2O3 Wt% 00.00 ---- 00.05 05
HfO2 contents Wt% 01-02.5 01-2.5 01-02.5 01-2.5
HCL contents Wt% 00.05   00.05  
DENSITY Gm/cm3   1.7   1.7
Viscosity, measured accordingl to DIN EN ISO 3219 at a shear rate of 100 s-1 * all contents are based on ignited material mPa s   2000   2000
Salient features of nano zirconia
Fineness of primary particles
:: low sintering temp due to nano structure
:: high BET-surface area
High purity
Chemically Inert
Superior rheological behaviour
Nano meter primary particles
:: Very slight solubility in acids and bases
:: High thermal stability
:: melting point appr.2700’C
:: low thermal conductivity and thermal expansion
Higher solid content up to (50%) in dispersion
nano zirconia finds use in
  • Catalysts, catalyst carrier
  • Optical interfaces - e. g. ferrules
  • Fine polishing (micrometer range)
  • Ceramic materials
  • Fuel cells
  • Sensors
  • Membranes
  • Dental
  • Glossy Inkjet Coatings
Highly crystallized ZrO2 particles can be dispersed into the various solvents at single nano-meters size distribution. Therefore ZrO2 nano-particles give extremely transparent dispersion with high refractive index
Important notice regarding this information
The statements and technical information contained in this document are based on our research and research of others.  However, this document is not contractual, and nothing in it, constitutes a warranty (expressed or implied) that the goods described are accurate and fit for a particular purpose of  the customer.  Purchasers are advised to make their own tests to determine the suitability. This specification supersedes any former publication and is subject to change without notice.
  Team RGe 
RGe may be contacted at its head quarters:
F-8, PHASE III, RIICO INDUSTRIAL AREA, Beawar 305901. Rajasthan – India.
Tel +91 1462 512340, fax +91 1462 226966,  Mobile +91 9414009700
Email: ssr@zirox.co.in, zirox50@gmail.com .
Website: www.zirox.co.in
Home | Profile | ProductsZirconia Technology | Inquiry | Site Map | Contact
© Copyright 2012 Raj Purohit Group of Enterprises